Quartz Ingot
- Materyèl Prensipal: 99.99% segondè-pite fusion kwatz (SiO₂)
- Fòm: Lingote solid silendrik/slab (ki pa trete)
- Nivo enpurte:<10ppm total metallic contaminants (Fe, Al, Ca, etc.)
- OH Kontni:<5ppm (low-hydroxyl grade available)
Dekri teren
Konpozisyon materyèl
Materyèl Prensipal:
99.99% segondè -pite fusion kwatz (SiO₂)
01
Fòm:
Solid silendrik/lingote dal (ki pa trete)
02
Nivo enpurte:
<10ppm total metallic contaminants (Fe, Al, Ca, etc.)
03
Kontni OH:
<5ppm (low-hydroxyl grade available)
04
Pwopriyete
|
Pwopriyete Fizik |
Valè |
|
Pite |
＞99.99% |
|
Dansite |
2.2g/cm3 |
|
Transparans |
＞90% |
|
Mohs dite |
5.5--6.5 |
|
Pwen deformation |
1280 degre |
|
Pwen ralantisman |
1780 degre |
|
Pwen recuit |
1250 degre |
|
Chalè Espesifik (20 - 350 degre) |
670J/kg. degre |
|
Kondiktivite tèmik (20 degre) |
1.4W/m. degre |
|
Kondiktivite chalè (w/mk, 1000 degre) |
1.0-1.2 |
|
Endèks refraktif |
1.4585 |
|
Koefisyan ekspansyon tèmik |
5.510 -7cm/cm. degre |
|
Tanperati k ap travay - cho |
1750--2050 degre |
|
Tanperati sèvis kout - tèm |
1300 degre |
|
Tanperati sèvis alontèm - |
1100 degre |
|
Pwopriyete chimik |
Valè |
|
Rezistan asid |
Asid fò (eksepte HF), alkali fò, solisyon òganik |
|
Tanperati wo Kowozyon reziste |
Ekselan |
|
Kontni enpurte metal |
<5 ppm |
|
Pwopriyete elektrik |
Valè |
|
Rezistivite |
7107Ω.cm |
|
Fòs izolasyon |
250 ~ 400Kv / cm |
|
Konstan Dielectric |
3.7~3.9 |
|
Koefisyan Absòbsyon Dielectric |
＜410-4 |
|
Koyefisyan Pèt Dielectric |
＜110-4 |
|
Pwopriyete mekanik |
Valè |
|
Fòs konpresyon |
1100MPa |
|
Fòs koube |
67MPa |
|
Fòs rupture |
48MPa |
|
Pwopòsyon Poisson a |
0.14~0.17 |
|
Modil Young la |
72000MPa |
|
Chea modil |
31000MPa |
Aplikasyon
Semiconductor:
- Konpozan chanm CVD
- Transpòtè pwosesis wafer
01
Faktori optik:
- Vid pou lantiy, prism, fenèt yo
- Konpozan litografi UV
02
Endistriyèl:
- Linèt ki gen gwo-tanperati
- Konpozan grave plasma
03
Rechèch:
- Substra optik lazè
- Fabrikasyon sistèm vakyòm
04
Avantaj
- Pi ba Defo: Mwens bul / enklizyon vs kwatz fonn
- Konsistans pakèt: tolerans dimansyon sere (± 0.5mm)
Lengote kwatz transparan ak lengote kwatz blan ki disponib
FAQ
Q1: Ki jan ingot kwatz konpare ak sentetik silica fusion?
A: pi wo rezistans tanperati men menm jan an pwopriyete optik. Silica sentetik gen pi bon transmisyon UV anba a 200nm.
Q2: Èske ingot kwatz ka itilize dirèkteman san D?
A: Non - mande pou koupe / polisaj pou aplikasyon fonksyonèl.
Q3: Ki tanperati maksimòm ki ka itilize?
A: 1100 degre kontinyèl (kout tèm -a 1450 degre). Pi wo pase 1200 degre, devitrifikasyon gradyèl rive.
Q4: Èske gen enpurte metalik?
A: klas estanda nou an gen<10ppm metals.
Baj popilè: Quartz ingot, Lachin kwatz ingot manifaktirè, Swèd, faktori
Voye rechèch